Titanium 6-2-4-2 vs. AISI 302B Stainless Steel

Titanium 6-2-4-2 belongs to the titanium alloys classification, while AISI 302B stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is AISI 302B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 8.6
45
Fatigue Strength, MPa 490
210
Poisson's Ratio 0.32
0.28
Reduction in Area, % 21
57
Shear Modulus, GPa 40
76
Shear Strength, MPa 560
410
Tensile Strength: Ultimate (UTS), MPa 950
580
Tensile Strength: Yield (Proof), MPa 880
230

Thermal Properties

Latent Heat of Fusion, J/g 400
320
Maximum Temperature: Mechanical, °C 300
930
Melting Completion (Liquidus), °C 1590
1400
Melting Onset (Solidus), °C 1540
1360
Specific Heat Capacity, J/kg-K 540
490
Thermal Conductivity, W/m-K 6.9
17
Thermal Expansion, µm/m-K 9.5
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 42
15
Density, g/cm3 4.6
7.7
Embodied Carbon, kg CO2/kg material 32
3.0
Embodied Energy, MJ/kg 520
43
Embodied Water, L/kg 210
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
210
Resilience: Unit (Modulus of Resilience), kJ/m3 3640
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 34
25
Strength to Weight: Axial, points 57
21
Strength to Weight: Bending, points 46
20
Thermal Diffusivity, mm2/s 2.8
4.4
Thermal Shock Resistance, points 67
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0 to 0.15
Chromium (Cr), % 0
17 to 19
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
65.7 to 73
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 1.8 to 2.2
0
Nickel (Ni), % 0
8.0 to 10
Nitrogen (N), % 0 to 0.050
0 to 0.1
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0.060 to 0.12
2.0 to 3.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4