Titanium 6-2-4-2 vs. AISI 430F Stainless Steel

Titanium 6-2-4-2 belongs to the titanium alloys classification, while AISI 430F stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is AISI 430F stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 8.6
23
Fatigue Strength, MPa 490
210
Poisson's Ratio 0.32
0.28
Reduction in Area, % 21
50
Shear Modulus, GPa 40
77
Shear Strength, MPa 560
340
Tensile Strength: Ultimate (UTS), MPa 950
540
Tensile Strength: Yield (Proof), MPa 880
310

Thermal Properties

Latent Heat of Fusion, J/g 400
280
Maximum Temperature: Mechanical, °C 300
870
Melting Completion (Liquidus), °C 1590
1430
Melting Onset (Solidus), °C 1540
1390
Specific Heat Capacity, J/kg-K 540
480
Thermal Conductivity, W/m-K 6.9
25
Thermal Expansion, µm/m-K 9.5
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 42
8.5
Density, g/cm3 4.6
7.7
Embodied Carbon, kg CO2/kg material 32
2.1
Embodied Energy, MJ/kg 520
29
Embodied Water, L/kg 210
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
110
Resilience: Unit (Modulus of Resilience), kJ/m3 3640
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 34
25
Strength to Weight: Axial, points 57
20
Strength to Weight: Bending, points 46
19
Thermal Diffusivity, mm2/s 2.8
6.7
Thermal Shock Resistance, points 67
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0 to 0.12
Chromium (Cr), % 0
16 to 18
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
79.2 to 83.9
Manganese (Mn), % 0
0 to 1.3
Molybdenum (Mo), % 1.8 to 2.2
0
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.060
Silicon (Si), % 0.060 to 0.12
0 to 1.0
Sulfur (S), % 0
0.15 to 0.35
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0