Titanium 6-2-4-2 vs. AWS BNi-4

Titanium 6-2-4-2 belongs to the titanium alloys classification, while AWS BNi-4 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is AWS BNi-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
180
Poisson's Ratio 0.32
0.31
Shear Modulus, GPa 40
67
Tensile Strength: Ultimate (UTS), MPa 950
430

Thermal Properties

Latent Heat of Fusion, J/g 400
340
Melting Completion (Liquidus), °C 1590
1070
Melting Onset (Solidus), °C 1540
980
Specific Heat Capacity, J/kg-K 540
470
Thermal Expansion, µm/m-K 9.5
11

Otherwise Unclassified Properties

Base Metal Price, % relative 42
60
Density, g/cm3 4.6
8.5
Embodied Carbon, kg CO2/kg material 32
10
Embodied Energy, MJ/kg 520
140
Embodied Water, L/kg 210
220

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 34
22
Strength to Weight: Axial, points 57
14
Strength to Weight: Bending, points 46
15
Thermal Shock Resistance, points 67
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0 to 0.050
Boron (B), % 0
1.5 to 2.2
Carbon (C), % 0 to 0.050
0 to 0.060
Cobalt (Co), % 0
0 to 0.1
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 1.5
Molybdenum (Mo), % 1.8 to 2.2
0
Nickel (Ni), % 0
91.4 to 95.5
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0.060 to 0.12
3.0 to 4.0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0 to 0.050
Zirconium (Zr), % 3.6 to 4.4
0 to 0.050
Residuals, % 0 to 0.4
0 to 0.5