Titanium 6-2-4-2 vs. AWS ENiCrMo-4

Titanium 6-2-4-2 belongs to the titanium alloys classification, while AWS ENiCrMo-4 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is AWS ENiCrMo-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 8.6
28
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
84
Tensile Strength: Ultimate (UTS), MPa 950
790

Thermal Properties

Latent Heat of Fusion, J/g 400
320
Melting Completion (Liquidus), °C 1590
1590
Melting Onset (Solidus), °C 1540
1530
Specific Heat Capacity, J/kg-K 540
410
Thermal Expansion, µm/m-K 9.5
12

Otherwise Unclassified Properties

Base Metal Price, % relative 42
70
Density, g/cm3 4.6
9.0
Embodied Carbon, kg CO2/kg material 32
13
Embodied Energy, MJ/kg 520
170
Embodied Water, L/kg 210
280

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 34
22
Strength to Weight: Axial, points 57
24
Strength to Weight: Bending, points 46
21
Thermal Shock Resistance, points 67
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0 to 0.020
Chromium (Cr), % 0
14.5 to 16.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
4.0 to 7.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 1.8 to 2.2
15 to 17
Nickel (Ni), % 0
49.9 to 63.5
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0.060 to 0.12
0 to 0.2
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Tungsten (W), % 0
3.0 to 4.5
Vanadium (V), % 0
0 to 0.35
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0 to 0.5