Titanium 6-2-4-2 vs. EN 1.7213 Steel

Titanium 6-2-4-2 belongs to the titanium alloys classification, while EN 1.7213 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is EN 1.7213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
73
Tensile Strength: Ultimate (UTS), MPa 950
500 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 300
420
Melting Completion (Liquidus), °C 1590
1460
Melting Onset (Solidus), °C 1540
1420
Specific Heat Capacity, J/kg-K 540
470
Thermal Conductivity, W/m-K 6.9
44
Thermal Expansion, µm/m-K 9.5
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 42
2.5
Density, g/cm3 4.6
7.8
Embodied Carbon, kg CO2/kg material 32
1.5
Embodied Energy, MJ/kg 520
20
Embodied Water, L/kg 210
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 34
24
Strength to Weight: Axial, points 57
18 to 55
Strength to Weight: Bending, points 46
18 to 38
Thermal Diffusivity, mm2/s 2.8
12
Thermal Shock Resistance, points 67
15 to 45

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0.22 to 0.29
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
96.7 to 98.1
Manganese (Mn), % 0
0.6 to 0.9
Molybdenum (Mo), % 1.8 to 2.2
0.15 to 0.3
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.060 to 0.12
0 to 0.3
Sulfur (S), % 0
0.020 to 0.040
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0