Titanium 6-2-4-2 vs. EN 2.4964 Cobalt

Titanium 6-2-4-2 belongs to the titanium alloys classification, while EN 2.4964 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is EN 2.4964 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 8.6
40
Fatigue Strength, MPa 490
220
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
86
Tensile Strength: Ultimate (UTS), MPa 950
960
Tensile Strength: Yield (Proof), MPa 880
390

Thermal Properties

Latent Heat of Fusion, J/g 400
290
Melting Completion (Liquidus), °C 1590
1630
Melting Onset (Solidus), °C 1540
1550
Specific Heat Capacity, J/kg-K 540
400
Thermal Conductivity, W/m-K 6.9
15
Thermal Expansion, µm/m-K 9.5
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
1.8

Otherwise Unclassified Properties

Density, g/cm3 4.6
9.6
Embodied Carbon, kg CO2/kg material 32
9.8
Embodied Energy, MJ/kg 520
140
Embodied Water, L/kg 210
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
310
Resilience: Unit (Modulus of Resilience), kJ/m3 3640
340
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 34
21
Strength to Weight: Axial, points 57
28
Strength to Weight: Bending, points 46
23
Thermal Diffusivity, mm2/s 2.8
3.9
Thermal Shock Resistance, points 67
25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0.050 to 0.15
Chromium (Cr), % 0
19 to 21
Cobalt (Co), % 0
46.4 to 58
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 3.0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 1.8 to 2.2
0
Nickel (Ni), % 0
9.0 to 11
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0.060 to 0.12
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Tungsten (W), % 0
14 to 16
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0