MakeItFrom.com
Menu (ESC)

Titanium 6-2-4-2 vs. Solder Alloy 714

Titanium 6-2-4-2 belongs to the titanium alloys classification, while solder alloy 714 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is solder alloy 714.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
51
Elongation at Break, % 8.6
17
Poisson's Ratio 0.32
0.36
Shear Modulus, GPa 40
19
Tensile Strength: Ultimate (UTS), MPa 950
52

Thermal Properties

Latent Heat of Fusion, J/g 400
62
Melting Completion (Liquidus), °C 1590
220
Melting Onset (Solidus), °C 1540
220
Specific Heat Capacity, J/kg-K 540
220
Thermal Conductivity, W/m-K 6.9
62
Thermal Expansion, µm/m-K 9.5
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
13
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
16

Otherwise Unclassified Properties

Density, g/cm3 4.6
7.4
Embodied Carbon, kg CO2/kg material 32
18
Embodied Energy, MJ/kg 520
300

Common Calculations

Stiffness to Weight: Axial, points 13
3.8
Stiffness to Weight: Bending, points 34
17
Strength to Weight: Axial, points 57
1.9
Strength to Weight: Bending, points 46
4.2
Thermal Diffusivity, mm2/s 2.8
37
Thermal Shock Resistance, points 67
3.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.050
0
Copper (Cu), % 0
0.3 to 0.7
Gold (Au), % 0
0 to 0.050
Hydrogen (H), % 0 to 0.015
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.25
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Molybdenum (Mo), % 1.8 to 2.2
0
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Silicon (Si), % 0.060 to 0.12
0
Silver (Ag), % 0
3.8 to 4.2
Tin (Sn), % 1.8 to 2.2
94.6 to 95.9
Titanium (Ti), % 83.7 to 87.2
0
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0