Titanium 6-2-4-2 vs. R05240 Alloy

Titanium 6-2-4-2 belongs to the titanium alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
150
Elongation at Break, % 8.6
25
Poisson's Ratio 0.32
0.36
Shear Modulus, GPa 40
57
Tensile Strength: Ultimate (UTS), MPa 950
270
Tensile Strength: Yield (Proof), MPa 880
170

Thermal Properties

Latent Heat of Fusion, J/g 400
210
Specific Heat Capacity, J/kg-K 540
190
Thermal Expansion, µm/m-K 9.5
6.8

Otherwise Unclassified Properties

Density, g/cm3 4.6
14
Embodied Water, L/kg 210
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
59
Resilience: Unit (Modulus of Resilience), kJ/m3 3640
90
Stiffness to Weight: Axial, points 13
6.3
Stiffness to Weight: Bending, points 34
13
Strength to Weight: Axial, points 57
5.4
Strength to Weight: Bending, points 46
6.8
Thermal Shock Resistance, points 67
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0 to 0.010
Hydrogen (H), % 0 to 0.015
0 to 0.0015
Iron (Fe), % 0 to 0.25
0 to 0.010
Molybdenum (Mo), % 1.8 to 2.2
0 to 0.020
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0 to 0.050
0 to 0.010
Oxygen (O), % 0 to 0.15
0 to 0.020
Silicon (Si), % 0.060 to 0.12
0 to 0.0050
Tantalum (Ta), % 0
57.9 to 65
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0 to 0.010
Tungsten (W), % 0
0 to 0.050
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0