Titanium 6-2-4-2 vs. S20433 Stainless Steel

Titanium 6-2-4-2 belongs to the titanium alloys classification, while S20433 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is S20433 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 8.6
46
Fatigue Strength, MPa 490
250
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
76
Shear Strength, MPa 560
440
Tensile Strength: Ultimate (UTS), MPa 950
630
Tensile Strength: Yield (Proof), MPa 880
270

Thermal Properties

Latent Heat of Fusion, J/g 400
280
Maximum Temperature: Mechanical, °C 300
900
Melting Completion (Liquidus), °C 1590
1400
Melting Onset (Solidus), °C 1540
1360
Specific Heat Capacity, J/kg-K 540
480
Thermal Conductivity, W/m-K 6.9
15
Thermal Expansion, µm/m-K 9.5
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 0.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 42
13
Density, g/cm3 4.6
7.7
Embodied Carbon, kg CO2/kg material 32
2.7
Embodied Energy, MJ/kg 520
39
Embodied Water, L/kg 210
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
230
Resilience: Unit (Modulus of Resilience), kJ/m3 3640
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 34
25
Strength to Weight: Axial, points 57
23
Strength to Weight: Bending, points 46
21
Thermal Diffusivity, mm2/s 2.8
4.0
Thermal Shock Resistance, points 67
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0 to 0.050
0 to 0.080
Chromium (Cr), % 0
17 to 18
Copper (Cu), % 0
1.5 to 3.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
64.1 to 72.4
Manganese (Mn), % 0
5.5 to 7.5
Molybdenum (Mo), % 1.8 to 2.2
0
Nickel (Ni), % 0
3.5 to 5.5
Nitrogen (N), % 0 to 0.050
0.1 to 0.25
Oxygen (O), % 0 to 0.15
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0.060 to 0.12
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.8 to 2.2
0
Titanium (Ti), % 83.7 to 87.2
0
Zirconium (Zr), % 3.6 to 4.4
0
Residuals, % 0 to 0.4
0