Titanium 6-5-0.5 vs. AWS BAg-4

Titanium 6-5-0.5 belongs to the titanium alloys classification, while AWS BAg-4 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is titanium 6-5-0.5 and the bottom bar is AWS BAg-4.

Titanium 6-5-0.5 (3.7155)AWS BAg-4 (P07400) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		100
Elastic (Young's, Tensile) Modulus, GPa		91

Poisson's Ratio		0.32
Poisson's Ratio		0.33

Shear Modulus, GPa		40
Shear Modulus, GPa		34

Tensile Strength: Ultimate (UTS), MPa		1080
Tensile Strength: Ultimate (UTS), MPa		150

Thermal Properties

Latent Heat of Fusion, J/g		410
Latent Heat of Fusion, J/g		140

Melting Completion (Liquidus), °C		1610
Melting Completion (Liquidus), °C		780

Melting Onset (Solidus), °C		1560
Melting Onset (Solidus), °C		670

Specific Heat Capacity, J/kg-K		550
Specific Heat Capacity, J/kg-K		330

Thermal Expansion, µm/m-K		9.4
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Density, g/cm³		4.5
Density, g/cm³		8.9

Embodied Carbon, kg CO₂/kg material		33
Embodied Carbon, kg CO₂/kg material		40

Embodied Energy, MJ/kg		540
Embodied Energy, MJ/kg		630

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		5.7

Stiffness to Weight: Bending, points		35
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		67
Strength to Weight: Axial, points		4.7

Strength to Weight: Bending, points		52
Strength to Weight: Bending, points		7.1

Thermal Shock Resistance, points		79
Thermal Shock Resistance, points		5.7

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452

Aluminum (Al), %		5.7 to 6.3
Aluminum (Al), %		0

Carbon (C), %		0 to 0.080
Carbon (C), %		0

Copper (Cu), %		0
Copper (Cu), %		29 to 31

Hydrogen (H), %		0 to 0.015
Hydrogen (H), %		0

Iron (Fe), %		0 to 0.2
Iron (Fe), %		0

Molybdenum (Mo), %		0.25 to 0.75
Molybdenum (Mo), %		0

Nickel (Ni), %		0
Nickel (Ni), %		1.5 to 2.5

Nitrogen (N), %		0 to 0.050
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.19
Oxygen (O), %		0

Silicon (Si), %		0 to 0.4
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		39 to 41

Titanium (Ti), %		85.6 to 90.1
Titanium (Ti), %		0

Zinc (Zn), %		0
Zinc (Zn), %		26 to 30

Zirconium (Zr), %		4.0 to 6.0
Zirconium (Zr), %		0

Residuals, %		0 to 0.4
Residuals, %		0 to 0.15