Titanium 6-5-0.5 vs. EN 1.4016 Stainless Steel

Titanium 6-5-0.5 belongs to the titanium alloys classification, while EN 1.4016 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is titanium 6-5-0.5 and the bottom bar is EN 1.4016 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Elongation at Break, % 6.7
22
Fatigue Strength, MPa 530
190
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
77
Shear Strength, MPa 630
330
Tensile Strength: Ultimate (UTS), MPa 1080
520
Tensile Strength: Yield (Proof), MPa 990
290

Thermal Properties

Latent Heat of Fusion, J/g 410
280
Maximum Temperature: Mechanical, °C 300
870
Melting Completion (Liquidus), °C 1610
1440
Melting Onset (Solidus), °C 1560
1400
Specific Heat Capacity, J/kg-K 550
480
Thermal Conductivity, W/m-K 4.2
25
Thermal Expansion, µm/m-K 9.4
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 41
8.5
Density, g/cm3 4.5
7.7
Embodied Carbon, kg CO2/kg material 33
2.1
Embodied Energy, MJ/kg 540
29
Embodied Water, L/kg 180
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71
95
Resilience: Unit (Modulus of Resilience), kJ/m3 4630
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 67
19
Strength to Weight: Bending, points 52
19
Thermal Diffusivity, mm2/s 1.7
6.7
Thermal Shock Resistance, points 79
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.7 to 6.3
0
Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 0
16 to 18
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.2
79.9 to 84
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0.25 to 0.75
0
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.19
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 85.6 to 90.1
0
Zirconium (Zr), % 4.0 to 6.0
0
Residuals, % 0 to 0.4
0