Titanium 6-5-0.5 vs. EN 1.4922 Stainless Steel

Titanium 6-5-0.5 belongs to the titanium alloys classification, while EN 1.4922 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is titanium 6-5-0.5 and the bottom bar is EN 1.4922 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 6.7
16
Fatigue Strength, MPa 530
330
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
76
Shear Strength, MPa 630
470
Tensile Strength: Ultimate (UTS), MPa 1080
770
Tensile Strength: Yield (Proof), MPa 990
550

Thermal Properties

Latent Heat of Fusion, J/g 410
270
Maximum Temperature: Mechanical, °C 300
720
Melting Completion (Liquidus), °C 1610
1460
Melting Onset (Solidus), °C 1560
1410
Specific Heat Capacity, J/kg-K 550
470
Thermal Conductivity, W/m-K 4.2
24
Thermal Expansion, µm/m-K 9.4
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 41
7.5
Density, g/cm3 4.5
7.8
Embodied Carbon, kg CO2/kg material 33
2.8
Embodied Energy, MJ/kg 540
40
Embodied Water, L/kg 180
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71
110
Resilience: Unit (Modulus of Resilience), kJ/m3 4630
770
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 67
27
Strength to Weight: Bending, points 52
24
Thermal Diffusivity, mm2/s 1.7
6.5
Thermal Shock Resistance, points 79
27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.7 to 6.3
0
Carbon (C), % 0 to 0.080
0.17 to 0.23
Chromium (Cr), % 0
10 to 12.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.2
83.5 to 88.2
Manganese (Mn), % 0
0.3 to 1.0
Molybdenum (Mo), % 0.25 to 0.75
0.8 to 1.2
Nickel (Ni), % 0
0.3 to 0.8
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.19
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 85.6 to 90.1
0
Vanadium (V), % 0
0.2 to 0.35
Zirconium (Zr), % 4.0 to 6.0
0
Residuals, % 0 to 0.4
0