Titanium 6-6-2 vs. 6005 Aluminum
Titanium 6-6-2 belongs to the titanium alloys classification, while 6005 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is titanium 6-6-2 and the bottom bar is 6005 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 68 |
| Elongation at Break, % | 6.7 to 9.0 | |
| 9.5 to 17 |
| Fatigue Strength, MPa | 590 to 670 | |
| 55 to 95 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 44 | |
| 26 |
| Shear Strength, MPa | 670 to 800 | |
| 120 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 1370 | |
| 190 to 310 |
| Tensile Strength: Yield (Proof), MPa | 1040 to 1230 | |
| 100 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 160 |
| Melting Completion (Liquidus), °C | 1610 | |
| 650 |
| Melting Onset (Solidus), °C | 1560 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 900 |
| Thermal Conductivity, W/m-K | 5.5 | |
| 180 to 200 |
| Thermal Expansion, µm/m-K | 9.4 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.1 | |
| 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 9.5 |
| Density, g/cm3 | 4.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 8.3 |
| Embodied Energy, MJ/kg | 470 | |
| 150 |
| Embodied Water, L/kg | 200 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 99 | |
| 27 to 36 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 34 | |
| 51 |
| Strength to Weight: Axial, points | 66 to 79 | |
| 20 to 32 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 28 to 38 |
| Thermal Diffusivity, mm2/s | 2.1 | |
| 74 to 83 |
| Thermal Shock Resistance, points | 75 to 90 | |
| 8.6 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.0 | |
| 97.5 to 99 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 0.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 5.0 to 6.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.6 to 0.9 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 82.8 to 87.8 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.15 |