Titanium 6-7 vs. AWS BAg-34

Titanium 6-7 belongs to the titanium alloys classification, while AWS BAg-34 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is titanium 6-7 and the bottom bar is AWS BAg-34.

Titanium 6-7 (R56700)AWS BAg-34 (P07380) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		89

Poisson's Ratio		0.33
Poisson's Ratio		0.33

Shear Modulus, GPa		45
Shear Modulus, GPa		34

Tensile Strength: Ultimate (UTS), MPa		1020
Tensile Strength: Ultimate (UTS), MPa		170

Thermal Properties

Latent Heat of Fusion, J/g		410
Latent Heat of Fusion, J/g		140

Melting Completion (Liquidus), °C		1700
Melting Completion (Liquidus), °C		720

Melting Onset (Solidus), °C		1650
Melting Onset (Solidus), °C		650

Specific Heat Capacity, J/kg-K		520
Specific Heat Capacity, J/kg-K		330

Thermal Expansion, µm/m-K		9.3
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Density, g/cm³		5.1
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		34
Embodied Carbon, kg CO₂/kg material		38

Embodied Energy, MJ/kg		540
Embodied Energy, MJ/kg		600

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		5.6

Stiffness to Weight: Bending, points		32
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		56
Strength to Weight: Axial, points		5.4

Strength to Weight: Bending, points		44
Strength to Weight: Bending, points		7.7

Thermal Shock Resistance, points		66
Thermal Shock Resistance, points		6.5

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460

Aluminum (Al), %		5.5 to 6.5
Aluminum (Al), %		0

Carbon (C), %		0 to 0.080
Carbon (C), %		0

Copper (Cu), %		0
Copper (Cu), %		31 to 33

Hydrogen (H), %		0 to 0.0090
Hydrogen (H), %		0

Iron (Fe), %		0 to 0.25
Iron (Fe), %		0

Molybdenum (Mo), %		6.5 to 7.5
Molybdenum (Mo), %		0

Niobium (Nb), %		6.5 to 7.5
Niobium (Nb), %		0

Nitrogen (N), %		0 to 0.050
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.2
Oxygen (O), %		0

Silver (Ag), %		0
Silver (Ag), %		37 to 39

Tantalum (Ta), %		0 to 0.5
Tantalum (Ta), %		0

Tin (Sn), %		0
Tin (Sn), %		1.5 to 2.5

Titanium (Ti), %		84.9 to 88
Titanium (Ti), %		0

Zinc (Zn), %		0
Zinc (Zn), %		26 to 30

Residuals, %		0
Residuals, %		0 to 0.15