Titanium Diboride vs. Granite
Titanium diboride belongs to the non-oxide engineering ceramics classification, while granite belongs to the natural stone. There are 16 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is titanium diboride and the bottom bar is granite.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 3540 | |
| 2200 |
| Elastic (Young's, Tensile) Modulus, GPa | 290 | |
| 70 |
| Flexural Strength, MPa | 380 | |
| 24 |
| Poisson's Ratio | 0.11 | |
| 0.25 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 39 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1270 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 840 |
| Thermal Conductivity, W/m-K | 58 | |
| 2.7 |
| Thermal Expansion, µm/m-K | 8.0 | |
| 7.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 2.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 35 | |
| 14 |
| Stiffness to Weight: Bending, points | 49 | |
| 48 |
| Strength to Weight: Axial, points | 17 | |
| 3.8 |
| Strength to Weight: Bending, points | 21 | |
| 9.0 |
| Thermal Diffusivity, mm2/s | 15 | |
| 1.1 |
| Thermal Shock Resistance, points | 8.7 | |
| 5.4 |