Type 1 Magnetic Alloy vs. ASTM A202 Steel

Both Type 1 magnetic alloy and ASTM A202 steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is ASTM A202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.0 to 38
17 to 18
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 500 to 830
590 to 670
Tensile Strength: Yield (Proof), MPa 220 to 790
350 to 360

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 5.6
1.4
Embodied Energy, MJ/kg 77
19
Embodied Water, L/kg 130
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 33 to 150
93 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 1690
330 to 350
Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 17 to 28
21 to 24
Strength to Weight: Bending, points 17 to 24
20 to 22
Thermal Shock Resistance, points 16 to 26
17 to 20

Comparable Variants