Type 1 Magnetic Alloy vs. C36000 Brass
Type 1 magnetic alloy belongs to the iron alloys classification, while C36000 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is C36000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 4.0 to 38 | |
| 5.8 to 23 |
| Poisson's Ratio | 0.3 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 830 | |
| 330 to 530 |
| Tensile Strength: Yield (Proof), MPa | 220 to 790 | |
| 140 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 170 |
| Melting Completion (Liquidus), °C | 1420 | |
| 900 |
| Melting Onset (Solidus), °C | 1370 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 380 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.1 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 23 |
| Density, g/cm3 | 8.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 77 | |
| 45 |
| Embodied Water, L/kg | 130 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 to 150 | |
| 25 to 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1690 | |
| 89 to 340 |
| Stiffness to Weight: Axial, points | 12 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 17 to 28 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 13 to 18 |
| Thermal Shock Resistance, points | 16 to 26 | |
| 11 to 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 60 to 63 |
| Iron (Fe), % | 50.7 to 56.5 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 2.5 to 3.7 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 43.5 to 46.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 32.5 to 37.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |