Type 2 Magnetic Alloy vs. AWS ERNiCrCoMo-1
Type 2 magnetic alloy belongs to the iron alloys classification, while AWS ERNiCrCoMo-1 belongs to the nickel alloys. They have 51% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is AWS ERNiCrCoMo-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 2.0 to 38 | |
| 28 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1420 |
| Melting Onset (Solidus), °C | 1370 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.9 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.2 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 75 |
| Density, g/cm3 | 8.4 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 10 |
| Embodied Energy, MJ/kg | 81 | |
| 140 |
| Embodied Water, L/kg | 140 | |
| 350 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 23 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 21 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0.8 to 1.5 |
| Carbon (C), % | 0 to 0.050 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 to 0.3 | |
| 20 to 24 |
| Cobalt (Co), % | 0 to 0.5 | |
| 10 to 15 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.5 |
| Iron (Fe), % | 48.2 to 53 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 8.0 to 10 |
| Nickel (Ni), % | 47 to 49 | |
| 42.7 to 61.2 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |