Type 2 Pewter vs. Solder Alloy 162
Both Type 2 pewter and solder alloy 162 are otherwise unclassified metals. They have 52% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 2 pewter and the bottom bar is solder alloy 162.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 52 | |
| 35 |
| Poisson's Ratio | 0.35 | |
| 0.4 |
| Shear Modulus, GPa | 19 | |
| 12 |
| Tensile Strength: Ultimate (UTS), MPa | 52 to 68 | |
| 41 |
Thermal Properties
| Latent Heat of Fusion, J/g | 69 | |
| 44 |
| Melting Completion (Liquidus), °C | 300 | |
| 220 |
| Melting Onset (Solidus), °C | 240 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 180 |
| Thermal Expansion, µm/m-K | 21 | |
| 25 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 9.4 |
| Embodied Energy, MJ/kg | 210 | |
| 160 |
| Embodied Water, L/kg | 1220 | |
| 830 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.9 | |
| 2.1 |
| Stiffness to Weight: Bending, points | 17 | |
| 12 |
| Strength to Weight: Axial, points | 2.0 to 2.6 | |
| 1.2 |
| Strength to Weight: Bending, points | 4.3 to 5.1 | |
| 2.8 |
| Thermal Shock Resistance, points | 3.4 to 4.4 | |
| 3.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 5.0 to 7.5 | |
| 0 to 0.2 |
| Arsenic (As), % | 0 to 0.050 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 1.5 to 3.0 | |
| 1.2 to 1.6 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.015 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.050 | |
| 47.3 to 49.3 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 90 to 93 | |
| 49.5 to 50.5 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 to 0.0010 |