Type 2 Pewter vs. Solder Alloy 301
Both Type 2 pewter and solder alloy 301 are otherwise unclassified metals. They have 42% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is Type 2 pewter and the bottom bar is solder alloy 301.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 13 to 23 | |
23 |
Elastic (Young's, Tensile) Modulus, GPa | 52 | |
40 |
Poisson's Ratio | 0.35 | |
0.34 |
Shear Modulus, GPa | 19 | |
15 |
Tensile Strength: Ultimate (UTS), MPa | 52 to 68 | |
55 |
Thermal Properties
Latent Heat of Fusion, J/g | 69 | |
55 |
Melting Completion (Liquidus), °C | 300 | |
140 |
Melting Onset (Solidus), °C | 240 | |
140 |
Specific Heat Capacity, J/kg-K | 220 | |
160 |
Thermal Expansion, µm/m-K | 21 | |
14 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.3 | |
8.7 |
Embodied Carbon, kg CO2/kg material | 12 | |
13 |
Embodied Energy, MJ/kg | 210 | |
210 |
Common Calculations
Stiffness to Weight: Axial, points | 3.9 | |
2.5 |
Stiffness to Weight: Bending, points | 17 | |
13 |
Strength to Weight: Axial, points | 2.0 to 2.6 | |
1.8 |
Strength to Weight: Bending, points | 4.3 to 5.1 | |
3.7 |
Thermal Shock Resistance, points | 3.4 to 4.4 | |
7.2 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.0010 |
Antimony (Sb), % | 5.0 to 7.5 | |
0 to 0.1 |
Arsenic (As), % | 0 to 0.050 | |
0 to 0.030 |
Bismuth (Bi), % | 0 | |
56.5 to 59 |
Cadmium (Cd), % | 0 | |
0 to 0.0020 |
Copper (Cu), % | 1.5 to 3.0 | |
0 to 0.050 |
Gold (Au), % | 0 | |
0 to 0.050 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 0 to 0.015 | |
0 to 0.020 |
Lead (Pb), % | 0 to 0.050 | |
0 to 0.070 |
Nickel (Ni), % | 0 | |
0 to 0.010 |
Silver (Ag), % | 0 | |
0 to 0.1 |
Tin (Sn), % | 90 to 93 | |
41 to 43 |
Zinc (Zn), % | 0 to 0.0050 | |
0 to 0.0010 |