Type 2 Pewter vs. C76200 Nickel Silver

Type 2 pewter belongs to the otherwise unclassified metals classification, while C76200 nickel silver belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is Type 2 pewter and the bottom bar is C76200 nickel silver.

Type 2 (L13912) Sheet Pewter UNS C76200 (CW405J) Nickel Silver

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		52
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.35
Poisson's Ratio		0.31

Shear Modulus, GPa		19
Shear Modulus, GPa		44

Tensile Strength: Ultimate (UTS), MPa		52 to 68
Tensile Strength: Ultimate (UTS), MPa		390 to 790

Thermal Properties

Latent Heat of Fusion, J/g		69
Latent Heat of Fusion, J/g		190

Melting Completion (Liquidus), °C		300
Melting Completion (Liquidus), °C		1030

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		980

Specific Heat Capacity, J/kg-K		220
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		19

Otherwise Unclassified Properties

Base Metal Price, % relative		75
Base Metal Price, % relative		29

Density, g/cm³		7.3
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		3.6

Embodied Energy, MJ/kg		210
Embodied Energy, MJ/kg		57

Embodied Water, L/kg		1220
Embodied Water, L/kg		310

Common Calculations

Stiffness to Weight: Axial, points		3.9
Stiffness to Weight: Axial, points		7.8

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		20

Strength to Weight: Axial, points		2.0 to 2.6
Strength to Weight: Axial, points		13 to 27

Strength to Weight: Bending, points		4.3 to 5.1
Strength to Weight: Bending, points		14 to 23

Thermal Shock Resistance, points		3.4 to 4.4
Thermal Shock Resistance, points		13 to 26

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460

Antimony (Sb), %		5.0 to 7.5
Antimony (Sb), %		0

Arsenic (As), %		0 to 0.050
Arsenic (As), %		0

Copper (Cu), %		1.5 to 3.0
Copper (Cu), %		57 to 61

Iron (Fe), %		0 to 0.015
Iron (Fe), %		0 to 0.25

Lead (Pb), %		0 to 0.050
Lead (Pb), %		0 to 0.1

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.5

Nickel (Ni), %		0
Nickel (Ni), %		11 to 13.5

Tin (Sn), %		90 to 93
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		24.2 to 32

Residuals, %		0
Residuals, %		0 to 0.5