Type 3 Magnetic Alloy vs. C48500 Brass
Type 3 magnetic alloy belongs to the nickel alloys classification, while C48500 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is Type 3 magnetic alloy and the bottom bar is C48500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 100 |
| Elongation at Break, % | 43 | |
| 13 to 40 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 70 | |
| 39 |
| Shear Strength, MPa | 380 | |
| 250 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 400 to 500 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 160 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 120 |
| Melting Completion (Liquidus), °C | 1370 | |
| 900 |
| Melting Onset (Solidus), °C | 1320 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 23 |
| Density, g/cm3 | 8.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 120 | |
| 46 |
| Embodied Water, L/kg | 220 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 56 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 120 to 500 |
| Stiffness to Weight: Axial, points | 12 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 17 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 18 | |
| 13 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 2.0 to 3.0 | |
| 0 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 4.0 to 6.0 | |
| 59 to 62 |
| Iron (Fe), % | 9.9 to 19 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 1.3 to 2.2 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 75 to 78 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 0 | |
| 34.3 to 39.2 |
| Residuals, % | 0 | |
| 0 to 0.4 |