C10400 Copper vs. EN 1.8897 Steel
C10400 copper belongs to the copper alloys classification, while EN 1.8897 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C10400 copper and the bottom bar is EN 1.8897 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 2.3 to 50 | |
| 20 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 160 to 240 | |
| 350 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 410 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 77 to 400 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1460 |
| Melting Onset (Solidus), °C | 1080 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 390 | |
| 49 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 2.2 |
| Density, g/cm3 | 9.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.6 |
| Embodied Energy, MJ/kg | 42 | |
| 22 |
| Embodied Water, L/kg | 340 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.5 to 91 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 690 | |
| 550 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 7.2 to 13 | |
| 20 |
| Strength to Weight: Bending, points | 9.4 to 14 | |
| 19 |
| Thermal Diffusivity, mm2/s | 110 | |
| 13 |
| Thermal Shock Resistance, points | 8.2 to 15 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 | |
| 0 to 0.16 |
| Copper (Cu), % | 99.9 to 99.973 | |
| 0 |
| Iron (Fe), % | 0 | |
| 96.8 to 99.98 |
| Manganese (Mn), % | 0 | |
| 0 to 1.7 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0 | |
| 0 to 0.050 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 0.027 to 0.050 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Vanadium (V), % | 0 | |
| 0 to 0.12 |
| Residuals, % | 0 to 0.050 | |
| 0 |