C10400 Copper vs. SAE-AISI M3 Class 2 Steel
C10400 copper belongs to the copper alloys classification, while SAE-AISI M3 class 2 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C10400 copper and the bottom bar is SAE-AISI M3 class 2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 410 | |
| 770 to 2210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 260 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1620 |
| Melting Onset (Solidus), °C | 1080 | |
| 1570 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 390 | |
| 26 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 25 |
| Density, g/cm3 | 9.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 12 |
| Embodied Energy, MJ/kg | 42 | |
| 180 |
| Embodied Water, L/kg | 340 | |
| 110 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 7.2 to 13 | |
| 26 to 74 |
| Strength to Weight: Bending, points | 9.4 to 14 | |
| 22 to 45 |
| Thermal Diffusivity, mm2/s | 110 | |
| 7.2 |
| Thermal Shock Resistance, points | 8.2 to 15 | |
| 24 to 69 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 1.2 to 1.3 |
| Chromium (Cr), % | 0 | |
| 3.8 to 4.5 |
| Copper (Cu), % | 99.9 to 99.973 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 75.8 to 82.3 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 4.8 to 6.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.45 |
| Silver (Ag), % | 0.027 to 0.050 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 5.0 to 6.8 |
| Vanadium (V), % | 0 | |
| 2.8 to 3.8 |
| Residuals, % | 0 to 0.050 | |
| 0 |