C10500 Copper vs. C96400 Copper-nickel
Both C10500 copper and C96400 copper-nickel are copper alloys. They have 67% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C10500 copper and the bottom bar is C96400 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 140 |
| Elongation at Break, % | 2.8 to 51 | |
| 25 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 51 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 400 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 75 to 400 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 260 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1240 |
| Melting Onset (Solidus), °C | 1080 | |
| 1170 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 390 | |
| 28 |
| Thermal Expansion, µm/m-K | 17 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 5.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 5.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 45 |
| Density, g/cm3 | 9.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 5.9 |
| Embodied Energy, MJ/kg | 42 | |
| 87 |
| Embodied Water, L/kg | 350 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 90 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 680 | |
| 250 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 6.8 to 12 | |
| 15 |
| Strength to Weight: Bending, points | 9.1 to 14 | |
| 16 |
| Thermal Diffusivity, mm2/s | 110 | |
| 7.8 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Copper (Cu), % | 99.89 to 99.966 | |
| 62.3 to 71.3 |
| Iron (Fe), % | 0 | |
| 0.25 to 1.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 28 to 32 |
| Niobium (Nb), % | 0 | |
| 0.5 to 1.5 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 0.034 to 0.060 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.050 | |
| 0 to 0.5 |