C10700 Copper vs. C15100 Copper
Both C10700 copper and C15100 copper are copper alloys. Their average alloy composition is basically identical. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C10700 copper and the bottom bar is C15100 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.2 to 50 | |
| 2.0 to 36 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell Superficial 30T Hardness | 27 to 70 | |
| 48 to 65 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 160 to 240 | |
| 170 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 410 | |
| 260 to 470 |
| Tensile Strength: Yield (Proof), MPa | 77 to 410 | |
| 69 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1100 |
| Melting Onset (Solidus), °C | 1080 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 390 | |
| 360 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 95 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 31 |
| Density, g/cm3 | 9.0 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 42 | |
| 43 |
| Embodied Water, L/kg | 390 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.9 to 91 | |
| 9.3 to 71 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 710 | |
| 21 to 890 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 7.2 to 13 | |
| 8.1 to 15 |
| Strength to Weight: Bending, points | 9.4 to 14 | |
| 10 to 15 |
| Thermal Diffusivity, mm2/s | 110 | |
| 100 |
| Thermal Shock Resistance, points | 8.2 to 15 | |
| 9.3 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 99.83 to 99.915 | |
| 99.8 to 99.95 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Silver (Ag), % | 0.085 to 0.12 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.050 to 0.15 |
| Residuals, % | 0 to 0.050 | |
| 0 to 0.1 |