C10700 Copper vs. C75700 Nickel Silver
Both C10700 copper and C75700 nickel silver are copper alloys. They have 65% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C10700 copper and the bottom bar is C75700 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.2 to 50 | |
| 3.2 to 22 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 45 |
| Shear Strength, MPa | 160 to 240 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 410 | |
| 590 to 610 |
| Tensile Strength: Yield (Proof), MPa | 77 to 410 | |
| 470 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 180 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1040 |
| Melting Onset (Solidus), °C | 1080 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 390 | |
| 40 |
| Thermal Expansion, µm/m-K | 17 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 30 |
| Density, g/cm3 | 9.0 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.6 |
| Embodied Energy, MJ/kg | 42 | |
| 56 |
| Embodied Water, L/kg | 390 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.9 to 91 | |
| 19 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 710 | |
| 930 to 1410 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 7.2 to 13 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 9.4 to 14 | |
| 19 |
| Thermal Diffusivity, mm2/s | 110 | |
| 12 |
| Thermal Shock Resistance, points | 8.2 to 15 | |
| 22 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 99.83 to 99.915 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 11 to 13 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Silver (Ag), % | 0.085 to 0.12 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 19.2 to 25.5 |
| Residuals, % | 0 to 0.050 | |
| 0 to 0.5 |