C10800 Copper vs. Grade Ti-Pd17 Titanium
C10800 copper belongs to the copper alloys classification, while grade Ti-Pd17 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C10800 copper and the bottom bar is grade Ti-Pd17 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 4.0 to 50 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 380 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 75 to 370 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 320 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1660 |
| Melting Onset (Solidus), °C | 1080 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 540 |
| Thermal Conductivity, W/m-K | 350 | |
| 21 |
| Thermal Expansion, µm/m-K | 17 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 92 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 92 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 36 |
| Embodied Energy, MJ/kg | 41 | |
| 600 |
| Embodied Water, L/kg | 310 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 88 | |
| 55 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 600 | |
| 180 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 35 |
| Strength to Weight: Axial, points | 6.8 to 12 | |
| 17 |
| Strength to Weight: Bending, points | 9.1 to 13 | |
| 21 |
| Thermal Diffusivity, mm2/s | 100 | |
| 8.8 |
| Thermal Shock Resistance, points | 7.8 to 13 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 99.95 to 99.995 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0.0050 to 0.012 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.9 to 99.96 |
| Residuals, % | 0 | |
| 0 to 0.4 |