C10800 Copper vs. C10500 Copper
Both C10800 copper and C10500 copper are copper alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is C10800 copper and the bottom bar is C10500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 4.0 to 50 | |
| 2.8 to 51 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 10 to 60 | |
| 10 to 62 |
| Rockwell F Hardness | 40 to 95 | |
| 40 to 99 |
| Rockwell Superficial 30T Hardness | 27 to 63 | |
| 27 to 67 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 150 to 200 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 380 | |
| 220 to 400 |
| Tensile Strength: Yield (Proof), MPa | 75 to 370 | |
| 75 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1080 |
| Melting Onset (Solidus), °C | 1080 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 350 | |
| 390 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 92 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 92 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 32 |
| Density, g/cm3 | 9.0 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 41 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 88 | |
| 11 to 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 600 | |
| 24 to 680 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 6.8 to 12 | |
| 6.8 to 12 |
| Strength to Weight: Bending, points | 9.1 to 13 | |
| 9.1 to 14 |
| Thermal Diffusivity, mm2/s | 100 | |
| 110 |
| Thermal Shock Resistance, points | 7.8 to 13 | |
| 7.8 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Copper (Cu), % | 99.95 to 99.995 | |
| 99.89 to 99.966 |
| Oxygen (O), % | 0 | |
| 0 to 0.0010 |
| Phosphorus (P), % | 0.0050 to 0.012 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.034 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.050 |