C12900 Copper vs. EN 1.7380 Steel
C12900 copper belongs to the copper alloys classification, while EN 1.7380 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C12900 copper and the bottom bar is EN 1.7380 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 2.8 to 50 | |
| 19 to 20 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 74 |
| Shear Strength, MPa | 150 to 210 | |
| 330 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 420 | |
| 540 to 550 |
| Tensile Strength: Yield (Proof), MPa | 75 to 380 | |
| 290 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 460 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1470 |
| Melting Onset (Solidus), °C | 1030 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 380 | |
| 39 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 98 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 98 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 3.8 |
| Density, g/cm3 | 9.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.8 |
| Embodied Energy, MJ/kg | 41 | |
| 23 |
| Embodied Water, L/kg | 330 | |
| 59 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 88 | |
| 87 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 640 | |
| 230 to 280 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 6.8 to 13 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 9.1 to 14 | |
| 19 |
| Thermal Diffusivity, mm2/s | 110 | |
| 11 |
| Thermal Shock Resistance, points | 7.8 to 15 | |
| 15 to 16 |
Alloy Composition
| Antimony (Sb), % | 0 to 0.0030 | |
| 0 |
| Arsenic (As), % | 0 to 0.012 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.0030 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.14 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 99.88 to 100 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 | |
| 94.6 to 96.6 |
| Lead (Pb), % | 0 to 0.0040 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 0 to 0.054 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tellurium (Te), % | 0 to 0.025 | |
| 0 |