C14181 Copper vs. ASTM A202 Steel

C14181 copper belongs to the copper alloys classification, while ASTM A202 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C14181 copper and the bottom bar is ASTM A202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
17 to 18
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Tensile Strength: Ultimate (UTS), MPa 210
590 to 670
Tensile Strength: Yield (Proof), MPa 130
350 to 360

Thermal Properties

Latent Heat of Fusion, J/g 210
260
Maximum Temperature: Mechanical, °C 200
410
Melting Completion (Liquidus), °C 1080
1450
Melting Onset (Solidus), °C 1080
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
52
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 41
19
Embodied Water, L/kg 310
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 28
93 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 69
330 to 350
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 6.5
21 to 24
Strength to Weight: Bending, points 8.8
20 to 22
Thermal Diffusivity, mm2/s 110
14
Thermal Shock Resistance, points 7.4
17 to 20