C14500 Copper vs. C14520 Copper
Both C14500 copper and C14520 copper are copper alloys. Their average alloy composition is basically identical. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C14500 copper and the bottom bar is C14520 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 12 to 50 | |
| 9.0 to 9.6 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 150 to 190 | |
| 170 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 330 | |
| 290 to 330 |
| Tensile Strength: Yield (Proof), MPa | 69 to 260 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1080 |
| Melting Onset (Solidus), °C | 1050 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 360 | |
| 320 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 94 | |
| 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 85 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 33 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 42 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 85 | |
| 24 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 300 | |
| 240 to 280 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 6.8 to 10 | |
| 9.0 to 10 |
| Strength to Weight: Bending, points | 9.1 to 12 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 100 | |
| 94 |
| Thermal Shock Resistance, points | 8.0 to 12 | |
| 10 to 12 |
Alloy Composition
| Copper (Cu), % | 99.2 to 99.596 | |
| 99.2 to 99.596 |
| Phosphorus (P), % | 0.0040 to 0.012 | |
| 0.0040 to 0.020 |
| Tellurium (Te), % | 0.4 to 0.7 | |
| 0.4 to 0.7 |