C14510 Copper vs. Solder Alloy 712
C14510 copper belongs to the copper alloys classification, while solder alloy 712 belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C14510 copper and the bottom bar is solder alloy 712.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 51 |
| Elongation at Break, % | 9.1 to 9.6 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.36 |
| Shear Modulus, GPa | 43 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 320 | |
| 51 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 62 |
| Melting Completion (Liquidus), °C | 1080 | |
| 220 |
| Melting Onset (Solidus), °C | 1050 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 220 |
| Thermal Conductivity, W/m-K | 360 | |
| 58 |
| Thermal Expansion, µm/m-K | 17 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 18 |
| Embodied Energy, MJ/kg | 42 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 17 |
| Strength to Weight: Axial, points | 9.2 to 10 | |
| 1.9 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 4.1 |
| Thermal Diffusivity, mm2/s | 100 | |
| 35 |
| Thermal Shock Resistance, points | 11 to 12 | |
| 3.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 99.15 to 99.69 | |
| 0.5 to 0.9 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0.010 to 0.030 | |
| 0 |
| Silver (Ag), % | 0 | |
| 3.3 to 3.7 |
| Tellurium (Te), % | 0.3 to 0.7 | |
| 0 |
| Tin (Sn), % | 0 | |
| 94.9 to 96.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |