C14510 Copper vs. C73500 Nickel Silver
Both C14510 copper and C73500 nickel silver are copper alloys. They have 72% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C14510 copper and the bottom bar is C73500 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 130 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 320 | |
| 380 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1140 |
| Melting Onset (Solidus), °C | 1050 | |
| 1090 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 360 | |
| 36 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 35 |
| Density, g/cm3 | 8.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 4.0 |
| Embodied Energy, MJ/kg | 42 | |
| 61 |
| Embodied Water, L/kg | 310 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 9.2 to 10 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 100 | |
| 10 |
| Thermal Shock Resistance, points | 11 to 12 | |
| 13 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Copper (Cu), % | 99.15 to 99.69 | |
| 70.5 to 73.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 16.5 to 19.5 |
| Phosphorus (P), % | 0.010 to 0.030 | |
| 0 |
| Tellurium (Te), % | 0.3 to 0.7 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 5.7 to 13 |
| Residuals, % | 0 | |
| 0 to 0.5 |