C14510 Copper vs. C77000 Nickel Silver

Both C14510 copper and C77000 nickel silver are copper alloys. They have 55% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C14510 copper and the bottom bar is C77000 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 43
46
Tensile Strength: Ultimate (UTS), MPa 300 to 320
420 to 800

Thermal Properties

Latent Heat of Fusion, J/g 210
200
Maximum Temperature: Mechanical, °C 200
180
Melting Completion (Liquidus), °C 1080
1050
Melting Onset (Solidus), °C 1050
1000
Specific Heat Capacity, J/kg-K 390
400
Thermal Conductivity, W/m-K 360
29
Thermal Expansion, µm/m-K 17
17

Otherwise Unclassified Properties

Base Metal Price, % relative 33
31
Density, g/cm3 8.9
8.3
Embodied Carbon, kg CO2/kg material 2.6
4.1
Embodied Energy, MJ/kg 42
63
Embodied Water, L/kg 310
300

Common Calculations

Stiffness to Weight: Axial, points 7.2
8.1
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 9.2 to 10
14 to 27
Strength to Weight: Bending, points 11 to 12
15 to 23
Thermal Diffusivity, mm2/s 100
8.8
Thermal Shock Resistance, points 11 to 12
15 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Copper (Cu), % 99.15 to 99.69
53.5 to 56.5
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0 to 0.050
0 to 0.050
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
16.5 to 19.5
Phosphorus (P), % 0.010 to 0.030
0
Tellurium (Te), % 0.3 to 0.7
0
Zinc (Zn), % 0
22.7 to 30
Residuals, % 0
0 to 0.5

Comparable Variants