C14510 Copper vs. C92200 Bronze

Both C14510 copper and C92200 bronze are copper alloys. They have 88% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C14510 copper and the bottom bar is C92200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 9.1 to 9.6
25
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
41
Tensile Strength: Ultimate (UTS), MPa 300 to 320
280
Tensile Strength: Yield (Proof), MPa 230 to 250
140

Thermal Properties

Latent Heat of Fusion, J/g 210
190
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 1080
990
Melting Onset (Solidus), °C 1050
830
Specific Heat Capacity, J/kg-K 390
370
Thermal Conductivity, W/m-K 360
70
Thermal Expansion, µm/m-K 17
19

Otherwise Unclassified Properties

Base Metal Price, % relative 33
32
Density, g/cm3 8.9
8.7
Embodied Carbon, kg CO2/kg material 2.6
3.2
Embodied Energy, MJ/kg 42
52
Embodied Water, L/kg 310
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 25 to 29
58
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
87
Stiffness to Weight: Axial, points 7.2
6.9
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 9.2 to 10
8.9
Strength to Weight: Bending, points 11 to 12
11
Thermal Diffusivity, mm2/s 100
21
Thermal Shock Resistance, points 11 to 12
9.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 99.15 to 99.69
86 to 90
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0 to 0.050
1.0 to 2.0
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0.010 to 0.030
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tellurium (Te), % 0.3 to 0.7
0
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0
Residuals, % 0
0 to 0.7