C14520 Copper vs. Grade 7 Babbitt Metal
C14520 copper belongs to the copper alloys classification, while grade 7 Babbitt Metal belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C14520 copper and the bottom bar is grade 7 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 26 |
| Poisson's Ratio | 0.34 | |
| 0.4 |
| Shear Modulus, GPa | 43 | |
| 9.1 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 25 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 48 |
| Melting Completion (Liquidus), °C | 1080 | |
| 270 |
| Melting Onset (Solidus), °C | 1050 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 150 |
| Thermal Expansion, µm/m-K | 17 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 4.4 |
| Embodied Energy, MJ/kg | 42 | |
| 62 |
| Embodied Water, L/kg | 310 | |
| 880 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 280 | |
| 12 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 1.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 9.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14 to 16 |
| Arsenic (As), % | 0 | |
| 0.3 to 0.6 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 99.2 to 99.596 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 71.9 to 76.4 |
| Phosphorus (P), % | 0.0040 to 0.020 | |
| 0 |
| Tellurium (Te), % | 0.4 to 0.7 | |
| 0 |
| Tin (Sn), % | 0 | |
| 9.3 to 10.7 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |