C14700 Copper vs. Nickel 684
C14700 copper belongs to the copper alloys classification, while nickel 684 belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C14700 copper and the bottom bar is nickel 684.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 9.1 to 35 | |
| 11 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 76 |
| Shear Strength, MPa | 160 to 190 | |
| 710 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 320 | |
| 1190 |
| Tensile Strength: Yield (Proof), MPa | 85 to 250 | |
| 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1370 |
| Melting Onset (Solidus), °C | 1070 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 75 |
| Density, g/cm3 | 8.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 10 |
| Embodied Energy, MJ/kg | 41 | |
| 140 |
| Embodied Water, L/kg | 310 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 to 65 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 31 to 280 | |
| 1610 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 7.3 to 10 | |
| 40 |
| Strength to Weight: Bending, points | 9.5 to 12 | |
| 30 |
| Thermal Shock Resistance, points | 8.4 to 12 | |
| 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 2.5 to 3.3 |
| Boron (B), % | 0 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 15 to 20 |
| Cobalt (Co), % | 0 | |
| 13 to 20 |
| Copper (Cu), % | 99.395 to 99.798 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 | |
| 0 to 4.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.75 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 0 | |
| 42.7 to 64 |
| Phosphorus (P), % | 0.0020 to 0.0050 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0.2 to 0.5 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 2.5 to 3.3 |
| Residuals, % | 0 to 0.1 | |
| 0 |