C15000 Copper vs. EN 1.3553 Steel
C15000 copper belongs to the copper alloys classification, while EN 1.3553 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C15000 copper and the bottom bar is EN 1.3553 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 460 | |
| 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 540 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1620 |
| Melting Onset (Solidus), °C | 980 | |
| 1570 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 370 | |
| 24 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 93 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 93 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 24 |
| Density, g/cm3 | 9.0 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.5 |
| Embodied Energy, MJ/kg | 43 | |
| 130 |
| Embodied Water, L/kg | 310 | |
| 96 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 6.2 to 14 | |
| 24 |
| Strength to Weight: Bending, points | 8.5 to 15 | |
| 21 |
| Thermal Diffusivity, mm2/s | 110 | |
| 6.4 |
| Thermal Shock Resistance, points | 7.3 to 17 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.78 to 0.86 |
| Chromium (Cr), % | 0 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 99.8 to 99.9 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 | |
| 80.7 to 83.7 |
| Manganese (Mn), % | 0 | |
| 0 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 4.7 to 5.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 6.0 to 6.7 |
| Vanadium (V), % | 0 | |
| 1.7 to 2.0 |
| Zirconium (Zr), % | 0.1 to 0.2 | |
| 0 |