C15000 Copper vs. C93400 Bronze
Both C15000 copper and C93400 bronze are copper alloys. They have 84% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C15000 copper and the bottom bar is C93400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 13 to 54 | |
| 9.1 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 43 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 460 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 45 to 460 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 150 |
| Melting Completion (Liquidus), °C | 1080 | |
| 950 |
| Melting Onset (Solidus), °C | 980 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 350 |
| Thermal Conductivity, W/m-K | 370 | |
| 58 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 93 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 93 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 32 |
| Density, g/cm3 | 9.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 43 | |
| 54 |
| Embodied Water, L/kg | 310 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 250 | |
| 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 8.7 to 910 | |
| 120 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 17 |
| Strength to Weight: Axial, points | 6.2 to 14 | |
| 8.3 |
| Strength to Weight: Bending, points | 8.5 to 15 | |
| 10 |
| Thermal Diffusivity, mm2/s | 110 | |
| 18 |
| Thermal Shock Resistance, points | 7.3 to 17 | |
| 10 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 99.8 to 99.9 | |
| 82 to 85 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 7.0 to 9.0 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 7.0 to 9.0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Zirconium (Zr), % | 0.1 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 1.0 |