C15100 Copper vs. SAE-AISI 1019 Steel
C15100 copper belongs to the copper alloys classification, while SAE-AISI 1019 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C15100 copper and the bottom bar is SAE-AISI 1019 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 2.0 to 36 | |
| 17 to 29 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 170 to 270 | |
| 300 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 470 to 520 |
| Tensile Strength: Yield (Proof), MPa | 69 to 460 | |
| 250 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1460 |
| Melting Onset (Solidus), °C | 1030 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 360 | |
| 52 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 95 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 1.8 |
| Density, g/cm3 | 9.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 43 | |
| 18 |
| Embodied Water, L/kg | 310 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.3 to 71 | |
| 82 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 890 | |
| 160 to 500 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 8.1 to 15 | |
| 17 to 18 |
| Strength to Weight: Bending, points | 10 to 15 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 100 | |
| 14 |
| Thermal Shock Resistance, points | 9.3 to 17 | |
| 15 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.15 to 0.2 |
| Copper (Cu), % | 99.8 to 99.95 | |
| 0 |
| Iron (Fe), % | 0 | |
| 98.7 to 99.15 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0.050 to 0.15 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 |