C15100 Copper vs. C26000 Brass
Both C15100 copper and C26000 brass are copper alloys. They have 70% of their average alloy composition in common.
For each property being compared, the top bar is C15100 copper and the bottom bar is C26000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.0 to 36 | |
| 2.5 to 66 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 30 to 64 | |
| 53 to 93 |
| Rockwell Superficial 30T Hardness | 48 to 65 | |
| 52 to 78 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Shear Strength, MPa | 170 to 270 | |
| 230 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 320 to 680 |
| Tensile Strength: Yield (Proof), MPa | 69 to 460 | |
| 110 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 140 |
| Melting Completion (Liquidus), °C | 1100 | |
| 950 |
| Melting Onset (Solidus), °C | 1030 | |
| 920 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 360 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 95 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 25 |
| Density, g/cm3 | 9.0 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 43 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.3 to 71 | |
| 6.1 to 420 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 890 | |
| 51 to 1490 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.1 to 15 | |
| 11 to 23 |
| Strength to Weight: Bending, points | 10 to 15 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 100 | |
| 38 |
| Thermal Shock Resistance, points | 9.3 to 17 | |
| 11 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Bismuth (Bi), % | 0 | |
| 0 to 0.0059 |
| Copper (Cu), % | 99.8 to 99.95 | |
| 68.5 to 71.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Zinc (Zn), % | 0 | |
| 28.1 to 31.5 |
| Zirconium (Zr), % | 0.050 to 0.15 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.3 |