C15100 Copper vs. C75400 Nickel Silver
Both C15100 copper and C75400 nickel silver are copper alloys. They have 65% of their average alloy composition in common.
For each property being compared, the top bar is C15100 copper and the bottom bar is C75400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.0 to 36 | |
| 2.0 to 43 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Rockwell B Hardness | 30 to 64 | |
| 60 to 90 |
| Rockwell Superficial 30T Hardness | 48 to 65 | |
| 27 to 77 |
| Shear Modulus, GPa | 43 | |
| 46 |
| Shear Strength, MPa | 170 to 270 | |
| 250 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 69 to 460 | |
| 130 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 190 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1080 |
| Melting Onset (Solidus), °C | 1030 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 360 | |
| 36 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 95 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 7.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 32 |
| Density, g/cm3 | 9.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.8 |
| Embodied Energy, MJ/kg | 43 | |
| 59 |
| Embodied Water, L/kg | 310 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.3 to 71 | |
| 12 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 890 | |
| 75 to 1450 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.1 to 15 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 10 to 15 | |
| 13 to 19 |
| Thermal Diffusivity, mm2/s | 100 | |
| 11 |
| Thermal Shock Resistance, points | 9.3 to 17 | |
| 12 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 99.8 to 99.95 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 14 to 16 |
| Zinc (Zn), % | 0 | |
| 16.2 to 22.5 |
| Zirconium (Zr), % | 0.050 to 0.15 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.5 |