C15500 Copper vs. C81400 Copper
Both C15500 copper and C81400 copper are copper alloys. They have a very high 99% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C15500 copper and the bottom bar is C81400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 3.0 to 37 | |
| 11 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 550 | |
| 370 |
| Tensile Strength: Yield (Proof), MPa | 130 to 530 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1090 |
| Melting Onset (Solidus), °C | 1080 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 350 | |
| 260 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 90 | |
| 60 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 91 | |
| 61 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 33 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 42 | |
| 45 |
| Embodied Water, L/kg | 360 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 84 | |
| 36 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 to 1210 | |
| 260 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.6 to 17 | |
| 11 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 13 |
| Thermal Diffusivity, mm2/s | 100 | |
| 75 |
| Thermal Shock Resistance, points | 9.8 to 20 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 0 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 0.6 to 1.0 |
| Copper (Cu), % | 99.75 to 99.853 | |
| 98.4 to 99.38 |
| Magnesium (Mg), % | 0.080 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0.040 to 0.080 | |
| 0 |
| Silver (Ag), % | 0.027 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |