C17200 Copper vs. Class 1 Tungsten
C17200 copper belongs to the copper alloys classification, while class 1 tungsten belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C17200 copper and the bottom bar is class 1 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 250 |
| Elongation at Break, % | 1.1 to 37 | |
| 5.7 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Rockwell C Hardness | 23 to 43 | |
| 28 |
| Shear Modulus, GPa | 45 | |
| 98 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 1380 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1250 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 120 |
| Thermal Conductivity, W/m-K | 110 | |
| 21 |
| Thermal Expansion, µm/m-K | 18 | |
| 5.1 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 | |
| 7.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 22 |
| Embodied Energy, MJ/kg | 150 | |
| 340 |
| Embodied Water, L/kg | 310 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 500 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5720 | |
| 660 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 14 |
| Strength to Weight: Axial, points | 15 to 44 | |
| 16 |
| Strength to Weight: Bending, points | 16 to 31 | |
| 14 |
| Thermal Diffusivity, mm2/s | 31 | |
| 12 |
| Thermal Shock Resistance, points | 16 to 46 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 1.8 to 2.0 | |
| 0 |
| Copper (Cu), % | 96.1 to 98 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 90 |
| Residuals, % | 0 to 0.5 | |
| 10 |