C17200 Copper vs. SAE-AISI P5 Steel
C17200 copper belongs to the copper alloys classification, while SAE-AISI P5 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C17200 copper and the bottom bar is SAE-AISI P5 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 1380 | |
| 370 to 1980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 250 |
| Melting Completion (Liquidus), °C | 980 | |
| 1460 |
| Melting Onset (Solidus), °C | 870 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 45 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 | |
| 8.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 150 | |
| 20 |
| Embodied Water, L/kg | 310 | |
| 56 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 44 | |
| 13 to 70 |
| Strength to Weight: Bending, points | 16 to 31 | |
| 15 to 45 |
| Thermal Diffusivity, mm2/s | 31 | |
| 12 |
| Thermal Shock Resistance, points | 16 to 46 | |
| 12 to 65 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 1.8 to 2.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 96.1 to 98 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.4 | |
| 95.7 to 97.8 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.6 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 to 0.35 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |