C17300 Copper vs. C72900 Copper-nickel
Both C17300 copper and C72900 copper-nickel are copper alloys. They have 77% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C17300 copper and the bottom bar is C72900 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 3.0 to 23 | |
| 6.0 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 45 |
| Shear Strength, MPa | 320 to 790 | |
| 540 to 630 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1380 | |
| 870 to 1080 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1200 | |
| 700 to 920 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 210 |
| Melting Completion (Liquidus), °C | 980 | |
| 1120 |
| Melting Onset (Solidus), °C | 870 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 29 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 | |
| 8.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 4.6 |
| Embodied Energy, MJ/kg | 150 | |
| 72 |
| Embodied Water, L/kg | 310 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 88 | |
| 49 to 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5410 | |
| 2030 to 3490 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 44 | |
| 27 to 34 |
| Strength to Weight: Bending, points | 16 to 31 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 32 | |
| 8.6 |
| Thermal Shock Resistance, points | 17 to 48 | |
| 31 to 38 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 1.8 to 2.0 | |
| 0 |
| Copper (Cu), % | 95.5 to 97.8 | |
| 74.1 to 78 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Lead (Pb), % | 0.2 to 0.6 | |
| 0 to 0.020 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.15 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 14.5 to 15.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.3 |