C17465 Copper vs. CC491K Bronze
Both C17465 copper and CC491K bronze are copper alloys. They have 86% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C17465 copper and the bottom bar is CC491K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 5.3 to 36 | |
| 13 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 930 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 120 to 830 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 160 |
| Melting Completion (Liquidus), °C | 1080 | |
| 980 |
| Melting Onset (Solidus), °C | 1030 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 370 |
| Thermal Conductivity, W/m-K | 220 | |
| 71 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 to 51 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 to 52 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 3.1 |
| Embodied Energy, MJ/kg | 64 | |
| 51 |
| Embodied Water, L/kg | 310 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 90 | |
| 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 64 to 2920 | |
| 67 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 6.7 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 9.7 to 29 | |
| 8.1 |
| Strength to Weight: Bending, points | 11 to 24 | |
| 10 |
| Thermal Diffusivity, mm2/s | 64 | |
| 22 |
| Thermal Shock Resistance, points | 11 to 33 | |
| 9.3 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Beryllium (Be), % | 0.15 to 0.5 | |
| 0 |
| Copper (Cu), % | 95.7 to 98.7 | |
| 81 to 87 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.3 |
| Lead (Pb), % | 0.2 to 0.6 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 1.0 to 1.4 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.25 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 | |
| 4.0 to 6.0 |
| Zirconium (Zr), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |