C17465 Copper vs. C48600 Brass
Both C17465 copper and C48600 brass are copper alloys. They have 61% of their average alloy composition in common.
For each property being compared, the top bar is C17465 copper and the bottom bar is C48600 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 5.3 to 36 | |
| 20 to 25 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 44 to 110 | |
| 55 to 58 |
| Shear Modulus, GPa | 44 | |
| 39 |
| Shear Strength, MPa | 210 to 540 | |
| 180 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 930 | |
| 280 to 360 |
| Tensile Strength: Yield (Proof), MPa | 120 to 830 | |
| 110 to 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 900 |
| Melting Onset (Solidus), °C | 1030 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 220 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 to 51 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 to 52 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 24 |
| Density, g/cm3 | 8.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 2.8 |
| Embodied Energy, MJ/kg | 64 | |
| 47 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 90 | |
| 55 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 64 to 2920 | |
| 61 to 140 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 9.7 to 29 | |
| 9.5 to 12 |
| Strength to Weight: Bending, points | 11 to 24 | |
| 12 to 14 |
| Thermal Diffusivity, mm2/s | 64 | |
| 36 |
| Thermal Shock Resistance, points | 11 to 33 | |
| 9.3 to 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Arsenic (As), % | 0 | |
| 0.020 to 0.25 |
| Beryllium (Be), % | 0.15 to 0.5 | |
| 0 |
| Copper (Cu), % | 95.7 to 98.7 | |
| 59 to 62 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 |
| Lead (Pb), % | 0.2 to 0.6 | |
| 1.0 to 2.5 |
| Nickel (Ni), % | 1.0 to 1.4 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 0 to 0.25 | |
| 0.3 to 1.5 |
| Zinc (Zn), % | 0 | |
| 33.4 to 39.7 |
| Zirconium (Zr), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |