C17500 Copper vs. SAE-AISI 1074 Steel
C17500 copper belongs to the copper alloys classification, while SAE-AISI 1074 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C17500 copper and the bottom bar is SAE-AISI 1074 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 6.0 to 30 | |
| 11 to 14 |
| Fatigue Strength, MPa | 170 to 310 | |
| 290 to 350 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 72 |
| Shear Strength, MPa | 200 to 520 | |
| 440 to 490 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 860 | |
| 740 to 820 |
| Tensile Strength: Yield (Proof), MPa | 170 to 760 | |
| 450 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 400 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1460 |
| Melting Onset (Solidus), °C | 1020 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 200 | |
| 50 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 to 53 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 24 to 54 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.8 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 73 | |
| 19 |
| Embodied Water, L/kg | 320 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 120 | |
| 77 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 2390 | |
| 550 to 860 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 9.7 to 27 | |
| 26 to 29 |
| Strength to Weight: Bending, points | 11 to 23 | |
| 23 to 25 |
| Thermal Diffusivity, mm2/s | 59 | |
| 14 |
| Thermal Shock Resistance, points | 11 to 29 | |
| 24 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 0.4 to 0.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.7 to 0.8 |
| Cobalt (Co), % | 2.4 to 2.7 | |
| 0 |
| Copper (Cu), % | 95.6 to 97.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0 | |
| 0.5 to 0.8 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.5 | |
| 0 |